CustomizationAvailable
After-Sales Service24 Hours After-Sale Service
ColorWhite
Model No.Aerogel Felt
Thermal Conductivity≤0.021W/M. K (at 25℃)
Maximum Operating Temperature1200 ℃
CombustibilityGrade a (Completely Non Combustible)
Hydropobic>99%
Vibration Mass Loss Rate≤1.0
Heating Permanent Line Change≥-2.0
Compression Rebound Rate>90
GuidelineInsulation
Density200 ± 30 Kg/M3
MaterialGlass Fiber, Silica
UsageIndustrial, Building, Pipeline, HVAC, Aerospace, a
Transport PackageRolls
SpecificationCustomized
TrademarkSkyboys
OriginZhejiang China
Hs Code5602900000
Production Capacity100000
Product CategoryGlass Fiber Battery Aerogel
CompositionGlass Fiber + Silicon Dioxide Aerogel
ApplicationEnergy Storage / Electric Furnaces / Petrochemicals
Product ModelXK-BX01
Compression Resilience> 90%
Thermal Insulation Performance700ºC≤350ºC(3.5mm)600ºC≤270ºC(2.0mm)500ºC≤250ºC(1.7mm)
Insulation∞
Withstand VoltageLeakage current under all conditions < 0.001mA
Hydrophobicity> 98%
Flame RetardantV-0
Fireproof RatingA1 (GB/T 25352-2010)
Operating Temperature-200°C to 650°C
Long-Term Shrinkage≤1% (650°C)
Water Absorption≤0.02%
AttributeSpecification
WidthCustomizable
ThicknessCustomizable
Max Operating Temperature1200°C
Thermal Conductivity @ 25°C≤0.021 W/m·K
Thermal Conductivity @ 300°C≤0.036 W/m·K
Vibration Compression Set Rate≥-1.0%
Heat Aging & Multi-Cycle Stability≥-0.0%
FlammabilityA Grade (Completely Non-combustible)
Hydrophobic Performance≥99%
Test Item1mm
Burn-Through Time20s
Dielectric Strength<0.1mA
Insulation Resistance≥500Ω
Flame Retardant LevelV0
Rohs 2.0Compliant
ReachCompliant